Վերնագիր: EFFECTIVE ANISOTROPY OF FE/SI THIN FILMS AND ITS NANOSTRUCTURE

Ստեղծողը:

A. Zolanvari ; H. Sadeghi ; J. Nezamdost

Տեսակ:

Article

Ամսագրի կամ հրապարակման վերնագիր:

Armenian Journal of Physics

Հրապարակման ամսաթիվ:

2009

Հատոր:

2

Համար:

4

ISSN:

1829-1171

Ծածկույթ:

295-301

Ամփոփում:

The 5 to 150 nm thicknesses of Fe layers have been deposited by evaporation method onto Si substrates. Magnetic properties of samples are measured by using Magnetic Force Microscopy (MFM) and Alternating Gradient Force Magnetometry (AGFM). Structural and magnetic properties of samples have been reported from domains structure in MFM images as well as hysteresis loops in AGFM results. The domains width in Fe samples with 100 nm thickness were estimated about 2–4 μm. The XRD patterns are also show the formation of β-FeSi2 phase after annealing up to 700°C. The calculated effective anisotropy for samples with different thicknesses also shows oscillations with increasing Fe layer thickness.

Ստեղծման ամսաթիվը:

2009

Նույնացուցիչ:

oai:arar.sci.am:23251

Բնօրինակի գտնվելու վայրը:

ՀՀ ԳԱԱ Հիմնարար գիտական գրադարան

Օբյեկտի հավաքածուներ:

Վերջին անգամ ձևափոխված:

May 19, 2021

Մեր գրադարանում է սկսած:

Feb 27, 2020

Օբյեկտի բովանդակության հարվածների քանակ:

0

Օբյեկտի բոլոր հասանելի տարբերակները:

https://arar.sci.am/publication/25963

Ցույց տուր նկարագրությունը RDF ձևաչափով:

RDF

Ցույց տուր նկարագրությունը OAI-PMH ձևաչափով։

OAI-PMH

Հրատարակության անուն Ամսաթիվ
EFFECTIVE ANISOTROPY OF FE/SI THIN FILMS AND ITS NANOSTRUCTURE May 19, 2021

Օբյեկտի տեսակ՝

Նման

Այս էջը օգտագործում է 'cookie-ներ'։ Ավելի տեղեկատվություն