Վերնագիր: SYNTHESIS AND CHARACTERIZATION OF CARBON-COATED Ni1-xCux FERROMAGNETIC NANOPARTICLES FOR SELF-REGULATING MAGNETIC HYPERTHERMIA

Ամսագրի կամ հրապարակման վերնագիր:

Armenian Journal of Physics

Հրապարակման ամսաթիվ:

2013

Հատոր:

6

Համար:

1

ISSN:

1829-1171

Ծածկույթ:

61-65

Ամփոփում:

Using the solid-state pyrolysis of metal-phthalocyanines (NiPc and CuPc), carbon-coated ferromagnetic Ni1-xCux (0 < x < 0.5) nanoparticles have been synthesized. The structure, composition and morphology of samples were investigated by means of scanning electron microscopy, energy-dispersive X-ray analysis, and powder X-ray diffraction. It is shown that the mean sizes of nanoparticles are varied from 30–40 nm to 350–400 nm depending on the pyrolysis conditions, and the thickness of carbon coating is about 10–20 nm. From X-band ferromagnetic resonance spectra it is obtained that the Curie temperature of nanoalloys can be varied in a wide range (from –150°C to 60°C) depending on the concentration of diamagnetic Cu atoms. The prepared samples can be used for self-regulating magnetic hyperthermia in oncology.

Ստեղծման ամսաթիվը:

2013-03-28

Նույնացուցիչ:

oai:arar.sci.am:23346

Բնօրինակի գտնվելու վայրը:

ՀՀ ԳԱԱ Հիմնարար գիտական գրադարան

Օբյեկտի հավաքածուներ:

Վերջին անգամ ձևափոխված:

May 19, 2021

Մեր գրադարանում է սկսած:

Feb 27, 2020

Օբյեկտի բովանդակության հարվածների քանակ:

0

Օբյեկտի բոլոր հասանելի տարբերակները:

https://arar.sci.am/publication/26081

Ցույց տուր նկարագրությունը RDF ձևաչափով:

RDF

Ցույց տուր նկարագրությունը OAI-PMH ձևաչափով։

OAI-PMH

Օբյեկտի տեսակ՝

Նման

Այս էջը օգտագործում է 'cookie-ներ'։ Ավելի տեղեկատվություն