Վերնագիր: РАЗРУШЕНИЕ ВОЛОКНИСТЫХ КОМПОЗИТНЫХ МАТЕРИАЛОВ ПРИ ДЛИТЕЛЬНОМ ЦИКЛИЧЕСКОМ ДЕФОРМИРОВАНИИ

Ծածկույթ:

80-85

Ամփոփում:

Researched the laminar composite materials failure mechanism under the static short-term and cyclic long-term loading. The analysis reasoning on the results of extensive experimental studies of strength, deformability and failure of glass-fiber, black-reinforced and organoplast materials under the stipulation that low-cycle and high-cycle fatigue are under the stretching, pressuring, symmetric stretching-pressuring cycle, simple bending and interlaminar shift. Considered the impact of symmetrical cut stress concentrator and central round outlet into the process of material development of failure. Studied the characteristics of crack birth process, their accumulation and extension depend upon the structure of armoured composite material and loading direction. Described three stage of fatigue crack beginning and spreading which is in aggregate bring to damage of composite. Discussed the questions of fibrous composite damaging empirical model considering the major characteristics of strained state and cyclic warping duration.

Հրատարակիչ:

National Academy of Sciences of Armenia

Ստեղծման ամսաթիվը:

2006

Նույնացուցիչ:

oai:arar.sci.am:169518

Ամսագրի կամ հրապարակման վերնագիր:

ՀՀ ԳԱԱ Տեղեկագիր: Մեխանիկա =Proceedings of National Academy of Sciences of Armenia: Mechanics

Հրապարակման ամսաթիվ:

2006

Հատոր:

vol. 59

Համար:

№ 3

ISSN:

0002-3051

Բնօրինակի գտնվելու վայրը:

ՀՀ ԳԱԱ Հիմնարար գիտական գրադարան

Օբյեկտի հավաքածուներ:

Վերջին անգամ ձևափոխված:

Sep 16, 2020

Մեր գրադարանում է սկսած:

Jun 22, 2020

Օբյեկտի բովանդակության հարվածների քանակ:

0

Օբյեկտի բոլոր հասանելի տարբերակները:

https://arar.sci.am/publication/186668

Ցույց տուր նկարագրությունը RDF ձևաչափով:

RDF

Ցույց տուր նկարագրությունը OAI-PMH ձևաչափով։

OAI-PMH

Օբյեկտի տեսակ՝

Նման

Այս էջը օգտագործում է 'cookie-ներ'։ Ավելի տեղեկատվություն